M. Fallahinejad Ghajari , S. Nabavi Razavi ,
Volume 20, Issue 1 (4 2007)
Abstract
Background and Aim: Extensive and continuous consumption of acidic drinks is the main cause of enamel erosion in human teeth. The purpose of this study was to compare the erosive potential of two Iranian drinks with those of two imported ones.
Materials and Methods: Two Iranian drinks (Cola Zamzam and Orange Zamzam) and two imported ones (Pepsi and Miranda) were studied in this experimental invitro study. 120 intact premolar teeth, extracted for orthodontic reasons were divided into 3 equal groups (A, B and C). Each group was exposed to one of the drinks for exposure times of: A: 15 minutes, B: 45 minutes and C: 12 hours. Each group was divided into 4 subgroups (each containing 10 teeth), which were exposed to 20 ml of one of the 4 drinks. The exposed surface was the same in all samples (a 5 mm in diameter semi circular window). The amount of Ca++ ion (mg/ml) added to each drink at the end of exposure time was estimated by atomic absorption spectrophotometer.
Results: 2 way ANOVA showed that the drinks were significantly different with regard to released Calcium ion. Time had significant effect on erosive potential. The two mentioned factors had significant interaction (P<0.001). The most erosive effect was seen in 12 hours in all of the drinks. The erosive effect of Orange Zamzam in 15 minutes and Pepsi in 45 minutes and 12 hours was significantly more than other groups (P<0.001).
Conclusions: Pepsi had the most long term erosive effect among the four drinks, and Cola Zamzam had the least erosive potential.
Elahe Soltanmohamadi Borujeni, Ali Bavi, Mohammad Aghaali, Ali Saleh, Aida Mehdipour,
Volume 37, Issue 0 (3-2024)
Abstract
Background and Aims: Strong bond between the ceramic brackets and ceramic veneers has an important role in cosmetic treatment. The purpose of this study was to investigate the effect of aging on the shear bond strength (SBS) of ceramic brackets bonded to zirconia after surface preparation by Neodymium-doped Yttrium Aluminum Garnet (Nd: YAG) laser or sandblasting with alumina.
Materials and Methods: This experimental study was conducted on 24 zirconia blocks and these blocks were randomly divided into two groups for surface preparation and each was sub-divided into three time intervals. Surface preparation was done by sandblasting with alumina: in SG1 (Immediately after sandblasting), SG2 (2 weeks after sandblasting), and SG3 (3 months after sandblasting) groups. For the Nd: YAG laser (1/5W, 20Hz, 10s) with non-contact mode: in LG4 (Immediately after laser), LG5 (2 weeks after laser), and LG6 (3 months after laser) groups. The ceramic brackets were bonded to the zirconia blocks. The SBS and adhesive remnant index (ARI) were evaluated and compared among test groups. Dara were analyzed using Mann Whitney test.
Results: There was no significant difference between the SBS of SG1 and LG4 (P=0.430), SG2 and LG5 (P=0.382) and SG3 and LG6 (P=0.326) groups. LG4 group showed the highest shear bond strength. After aging (2 weeks and 3 months), the laser groups showed higher SBS. There was no significant difference in the ARI between SG1 and LG4 (P=0.220), SG2 and LG5 (P=0.154), SG3 and LG6 (P=0.527) groups.
Conclusion: No significant difference was observed between the Nd: YAG laser and sandblasted groups in terms of SBS and ARI over time. Therefore, Nd: YAG laser could be used as a surface treamnet method in Zirconia crowns for bonding to ceramic brackets.