Showing 10 results for Daneshkazemi
Alireza Daneshkazemi, Abdolrahim Davari, Majid Mousavinasab, Alireza Zahedifar,
Volume 26, Issue 2 (5-2013)
Abstract
Background and Aims: Today, use of adhesive systems is the most common materials in restorative dental procedures. The aim of this study was to evaluate the effect of different air-drying periods on the microtensile bond strength of composite to dentin using adhesive.
Materials and Methods: 15 sound molar teeth were selected. The an occlusal surfaces of teeth were removed with silicon carbide disks (3M/USA) to reach flat surface of dentin. Then according to the air drying of solvent, the teeth were divided to five groups. After 5 sec etching and rinsing for 15 sec , the teeth were air dried for 3 sec . Then Singlebond (3M) was used with different air-drying times (0s, 2s, 5s, 10s, 30s) and cured. Then after insertion and curing of Saremco (microhybrid low shrinkage/Switzerland) composite, the teeth were thermocycled for 500 cycles. Then hour glass slabs with 1 mm2 interface was created. Specimens were then subjected to µTBS force until fracture. Data were analyzed using ANOVA and Bonferroni tests.
Results: Statistical tests showed that there were significant differences between bond strength of groups (P=0.002). The mean of µTBS for the 2 Sec and 30 Sec evaporating time was the most and the least vawes, respectively.
Conclusion: An optimum air-drying time for solvent evaporation was the lowest time recommended by the manufacturer. Over and under evaporation time decreased µTBS significantly.
Davari Abdolrahim , Daneshkazemi Alireza , Modaber Maryam , Malekzadeh Mohammad ,
Volume 27, Issue 4 (1-2015)
Abstract
Background and Aims: The most effective preventing tooth decay method is fluoride compounds applications. Some studies suggested that APF gels caused changes on the superficial physical properties of composite. Therefore, the purpose of this study was to evaluate the marginal microleakage of class V composite restorations before and after AFP gel application.
Materials and Methods: The class V cavities in buccal surfaces of 45 molar teeth were made in such a way that occlusal margin was placed in enamel and cervical margin in cement. In group 1, at first fluoride-therapy and then cavity preparation and restoration by composite resin was done. In group 2, at first the class V cavities were prepared and restored, then fluoride-therapy was carried out. In group 3, cavities were prepared and restored with no fluoride-therapy. The dye penetration rate in occlusal and cervical margins was examined by stereomicroscope. Data were statistically analyzed using Kruskal-Wallis and Mann-Whitney test.
Results: There was no statistically significant difference between groups ( P=0.975).
Conclusion: Fluoride-therapy using AFP gel before and after class V composite restorations, had no significant effect on the microleakage of dentin and enamel margins.
Abdolrahim Davari, Soghra Yassaei, Alireza Daneshkazemi, Mohadeseh Khosravanian,
Volume 28, Issue 2 (7-2015)
Abstract
Background and Aims: Orthodontic bracket failure during treatment is a common problem. With the introduction of low shrinkage composites the question is that whether: this sufficient has coefficient bond strength for bonding bracket during orthodontic treatment. The aim of this study was to compare the shear bond strength (SBS) of silorane-based and metacrylate-based composites to metal brackets.
Materials and Methods: 30 human premolar teeth were collected and divided into 2 groups. In group 1, 15 orthodontic brackets were bonded using silorane-based composite, in group 2, 15 orthodontic brackets were bonded using metacrylate-based composite. The shear bond strength of each specimen was determined in an Instron machine. Amount of residual adhesive remaining on each tooth was evaluated using a stereomicroscope. Data were analyzed using T-test to compare the shear bond strength between groups and LSD method to compare the Adhesive Remnant Index (ARI) scores.
Results: There was significant difference in the SBS between the test groups (P<0.001). The mean bond strength of bonding brackets to silorane-based composite was (42.42 ± 7.03) MPa, and the mean bond strength of bonding brackets metacrylate-based composite was (21.08±2.97 ) MPa. No significant difference in the ART was found between groups (P=0.66).
Conclusion: Silorane-based composite provided higher bond strength to orthodontic metal brackets.
Alireza Daneshkazemi, Abdolrahim Davari, Farnaz Farahat, Neda Pazhoohi,
Volume 28, Issue 2 (7-2015)
Abstract
Background and Aims: The purpose of this study was to compare the effect of chlorhexidine 2%, ethanol 70% and sodium ascorbate 10% and delayed bonding for 1 week on the shear bond strength of composite resin to enamel after bleaching.
Materials and Methods: 90 human central incisors were divided into 6 equal groups: Group 1: no bleaching Group 2: bleaching with carbamide peroxide 45% for 45 minutes Group 3: bleaching + restoring specimens in distilled water for 1 week. In group 4, 5 and 6, after bleaching, 1 cc of chlorhexidine 2%, ethanol 70% and sodium ascorbate 10% were applied for 15 minutes. Composite cylinders were bonded on the buccal surfaces. Specimens were thermocycled for 1000 cycles and the shear bond strength test was done. Specimens were examined under stereomicroscope and SEM. Data were analyzed a sign ANOVA and Bonferroni test.
Results: The shear bond strength values were not significantly lower in the bleached teeth (group 3, 4, 5 and 6) than that of negative control group (group 1) (P=1.000, P=0.069, P=0.081, P=1.000) Bonferroni test results show significant difference between test groups (3, 4, 5 and 6) and group 2 (P<1.000, P=0.007, P=0.008, P<1.000) Under SEM, resin tags in group 2 was thinner and lesser than group 3, 4, 5 and 6. The most adhesive failures were in group 2.
Conclusion: Bleaching with carbamide peroxide and immediate bonding of composite decreased the shear bond strength. Sodium ascorbate 10% and delayed bonding for 1 week were the most effective way.
Rahelesadat Mirseifi Nejad Naini, Alireza Daneshkazemi, Fahime Shafiee,
Volume 31, Issue 2 (9-2018)
Abstract
Background and Aims: Increased tooth sensitivity is a common dental problem. One of the mechanisms of dentin hypersensitivity treatment is blocking dentinal tubules. The aim of this study was to compare the average closing dentinal tubules affected by carbonated Nano-hydroxyapatite and fluoride toothpaste using scanning electron microscope (SEM).
Materials and Methods: The enamel of gingival buccal crown surfaces of 42 sound maxillary premolars teeth were removed until the dentin surfaces were exposed. The dentine specimens of 3×3 mm were prepared. The specimens were washed by distilled water after etching and randomly divided into 6 groups. 3 groups were interfered with the carbonated nano-hydroxyapatite toothpaste and the other three groups interfered with Colgate toothpaste in 3, 7 and 14 days. The samples were examined by SEM to check the status of dentinal tubules. Then, they were evaluated by two researchers according to the Hulsmann index. Data were analyzed by using SPSS23 software and Kruskal-Wallis statistical test. The significance level of 0.05 was considered.
Results: The amount of dentinal tubules closure by the two toothpastes was significantly different. This difference was higher in the hydroxyapatite toothpaste than fluoride which were (P=0.024, 0.004 and 0.000), respectively. There were no significant differences among the groups in 3,7 and 14 days (P=0.230, 0.069, 0.537).
Conclusion: The toothpaste containing carbonated nano structural hydroxyapatite was more successful in closing dentinal tubules than Colgate toothpaste in short period of time.
Abdolrahim Davari, Alireza Daneshkazemi, Farnaz Frahat, Fatemeh Kohestani,
Volume 32, Issue 1 (7-2019)
Abstract
Background and Aims: Despite patient’s demand increased for tooth color restorations, the stable bond between dentin and composite is a challenge in dentistry. Dentin protease activation is responsible for dentin-resin bond failure. The aim of this study was to determine the best pretreatment agent to inhibit matrix metalloproteinase and increase resin-dentin bond durability.
Materials and Methods: After collecting 24 intact third molars, the dentin surfaces were exposed immediately under DEJ. After acid etching of dentin rewetting was done with CHX 2%, EDC 0.3 M for 60 and water (control group). Then the adhesive (Single bond, 3M ESPE, USA) and composite (Filtek Z250 XT, 3M ESPE, USA) were applied. 48 sectioned dentinal specimens were prepared. The specimens were divided into 3 groups. Each group was divided into 2 sub groups (n=8). In half of each group, the micro tensile bond strength test was done immediately and another part half 6 months. Then, the specimens were evaluated by stereomicroscope and SEM. Statistical analysis was performed using SPSS23 software, two-way ANOVA and multiple Tukey and T-test comparisons. P<0.05 was considered as a significant level.
Results: There were not significant differences between immediate micro tensile bond strength of CHX, EDC and control groups (P=0.97). However, there was significant differences between CHX, EDC compared with the control group (P≤0.0001). Comparison between the immediate and 6-month bond strengths in each group, only in EDC group, there was no significant after 6 months’ difference (P=0.64).
Conclusion: EDC and CHX t did not have any effect on the immediate microtensile bond strength. After 6 months, EDC prevented bond strength deterioration, but the bond strength was decreased after CHX usage.
Abdolrahim Davari, Alireza Daneshkazemi, Mahsan Sheshmani, Haleh Karami, Elham Motallebi,
Volume 32, Issue 3 (11-2019)
Abstract
Background and Aims: The bleaching agents can lead to color and translucency changes in composite resins. Due to the increasing use of the nano composites and the silorane-based composites, this study aimed at examining the color and translucency changes of these restorations after bleaching agents.
Materials and Methods: In this experimental - laboratory study, 198 composite discs were divided into three groups of 66 specimens using three types of composite: the microhybrid composite Z250, the nanohybrid composite Z350 and the silorane-based composite P90. After acid etching, half of the specimens in each group were covered by a resin rebounding agent. Then, the color and translucency assessment was done by reflectance spectrophotometer, using CIE LAB system. Each group was divided into three subgroups of bleaching agents: the 40% hydrogen peroxide and 20% carbamide peroxide bleaching agents and the control group. After applying bleaching agents, the final color and translucency changes were assessed. Data were analyzed using Mann Whitney and Kruskal Wallis tests.
Results: The effect of composite and bleaching agent type and bonding agent were significant (P<0.001). The color changes in the microhybrid composite were higher than nanohybrid and silorane-based composites (P<0.001) (∆E>3.3). Also, the color changes by 20% carbamide peroxide were higher than that of hydrogen peroxide and control groups (P<0.001). The results of translucency changes were generally consistent with color-change measurements (∆E>3.3).
Conclusion: According to the present study, the most color changes appeared in the microhybrid composite and by 20% carbamide peroxide bleaching agent. Rebound samples were generally less affected by bleaching agents. The least color and translucency changes were related to nanohybrid composites.
Alireza Daneshkazemi, Abdolrahim Davari, Motahareh Amiri, Fatemeh Mirhosseini,
Volume 33, Issue 1 (7-2020)
Abstract
Background and Aims: Erosion is the chemical dissolution of a tooth by acid without bacterial involvement. The purpose of the current study was to investigate the effect of resin infiltration (Icon), MI paste plus, and Nd:YAG laser on the enamel microhardness.
Materials and Methods: 40 enamel samples were obtained from the third molar tooth. Primary microhardness was measured in all specimens. Then, erosion was created using hydrochloride acid on the surfaces of enamel and the microhardness values were measured. The samples were randomly divided into four groups. G1: MI paste plus, G2: MI paste plus+ Nd:YA laser, G3: ICON without etching, G4: ICON with etching. Erosion was induced again by hydrochloric acid and then subjected to thermocycling. Finally, the microhardness of the samples was measured. Statistical analysis was performed using SPSS23 software, one-way ANOVA, multiple Tukey and T-test comparisons. P<0.05 was considered as a significant level.
Results: The microhardness increased in the third stage compared to the second stage in all groups, which was statistically significant (P<0.000). Also, the comparison of the increase of microhardness among groups, except second group with the fourth group, was statistically significant.
Conclusion: All the materials used in this study significantly increased the microhardness of the eroded enamel.
Alireza Daneshkazemi, Abdolrahim Davari, Zahra Usefi, Niloofar Fallah, Solmaz Ghanbarnejad, Pedram Daneshkazemi,
Volume 33, Issue 3 (10-2020)
Abstract
Background and Aims: Adding nanoparticles to dental composite resins, could reduce bacterial adhesion and secondary caries. Thermocycling can resemble in-vitro conditions to the oral environment. The aim of this study was to determine the effect of thermocycling on the microleakage of a mixture of copper oxide nanoparticles and flowable composite.
Materials and Methods: In this in-vitro study, 88 premolar teeth were divided into eight groups based on the application of copper oxide nanoparticles with concentrations of 0.1% and 0.3% w/w and thermocycling by 0, 1000, 5000 and 15,000 cycles. The occlusal grooves of the teeth were sealed with the mixture of flowable composite and copper oxide nanoparticles, and the teeth were thermocycled. Next, the teeth were immersed in methylene blue 2% solution for 24 hrs and were cut and the microleakage was evaluated by a stereomicroscope (hp/USA). Data were analyzed using Kruskal-Wallis and Mann-Whitney tests at the significance level of 0.05.
Results: In the groups with 0.1 % copper oxide nanoparticles, the mean microleakage increased significantly with increasing the number of thermocycling rounds (P=0.032). The difference in the microleakage between the groups exposed to 0 and 15,000 termocycling was significant (P=0.019). However, thermocycling had no significant effect on the microleakage of groups with concentration of 0.3% (P=0.780). The specimens subjected to the 0, 1000, 5000 and 15000 thermocycling in two concentrations of copper oxide nanoparticles showed no significant difference in the microleakage.
Conclusion: In groups containing copper oxide nanoparticles with a concentration of 0.1%, the microleakage increased by increasing the number of thermocycling up to 15,000 cycles compared to the control group. However, this did not have significant effect for the concentration of 0.3% copper oxide nanoparticles.
Alireza Omrani, Pedram Daneshkazemi, Amir Mansour Shirani, Mohammad Amin Habibi,
Volume 34, Issue 0 (5-2021)
Abstract
Background and Aims: Temporomandibular joint disorders (TMDs) are one of the most common causes of the patient's referral to dental clinics. Considering the role of related factors in its creation, the purpose of this study was to investigate the relative frequency of factors related to temporomandibular disorders in patients aged 20 to 50 years referred to dental clinics in Isfahan in 1397.
Materials and Methods: In this descriptive and analytical study, 324 patients referred to Isfahan dental clinics in 1397 were randomly included. Factors related to TMD and demographic factors of patients were recorded with clinical examination by a trained dentist and self-declaration of patients in the data collection form. The frequency and relevance were analysed by SPSS 22 software and chi-square, fisher and logistic regression statistic tests.
Results: At least one of the TMD related factors was present in 40.7% of the subjects, which the most common factors related to TMD was posterior edentulousness (49.7%). History of jaw dislocation was more common in men (P=0.014) and the frequency of posterior edentulousness was more common in in women (P=0.003). As the age increased, the frequency of posterior edentulousness (P=0.000) and earache (P=0.009) increased. The frequency of posterior edentulousness was higher in housekeepers (P=0.000), the frequency of earache was higher in employees (P=0.005) and the history of jaw dislocation was higher in self-employed persons (P=0.047). |
Conclusion: The high prevalence of TMD and related factors, such as a history of jaw dislocation, posterior edentulousness, earache, and clenching, requires attention to be identified and treat these problems.