Journal of Dental Medicine

---

Background and Aim: All ceramic, inlay-retained resin bonded fixed partial denture is a conservative method for replacement of missing teeth, because of minimal tooth reduction. The connector between the retainer and the pontic is the weak point of these bridges. Reinforcement of ceramic core will increase the clinical longevity. The aim of this study was to determine the effect of zirconia on flexural strength of IPS Empress 2 core ceramic.

Materials and Methods: In this experimental in vitro study, twenty eight bar shape specimens (17´3.1´3.1 mm) were made of four different materials: (1) Slip casting in-ceram alumina core (control group) (2) Hot-pressed lithium disilicate core ceramic (IPS Empress 2) (3) IPS Empress 2 with cosmopost (zirconia post) inserted longitudinally in the center of the bar (4) IPS Empress 2 with cosmopost (zirconia post) inserted longitudinally in bottom of the bar. Specimens were subjected to three-point flexure loading with the span of 15mm, at a cross-head speed of 0.5 mm/min. Failure loads were recorded and analyzed using one-way ANOVA and Tomhane Post-hoc tests and p<0.05 was set as the level of significance. Fractured surfaces were then observed by scanning electron microscope (SEM). Four additional samples were made as the third group, and zirconia-IPS interface was observed by SEM before fracture.

Results: Mean values and standard deviations of three point flexural strengths of groups 1 to 4, were: 378.4±44.6, 258.6±27.5, 144.3±51.7, 230±22.3 MPa respectively. All the groups were statistically different from each other (P<0.05), except groups 2 and 4. The flexural strengths of groups 2, 3, 4 were significantly lower than group 1. Group 3 had the lowest flexural strength. SEM analysis showed that the initiated cracks propagated in the interface of zirconia post and IPS Empress 2 ceramic.

Conclusion: Based on the results of this study, inserting zirconia post (cosmopost) in IPS Empress 2 ceramic does not reinforce all-ceramic inlay retained resin bonded fixed partial dentures.

---

Background and Aims: This ex vivo study was done to evaluate the effect of different adhesive systems on microleakage of class V composite restorations.
Materials and Methods: Thirty extracted human third molar teeth were selected and class V cavities were prepared (3×3×1.5 mm) on buccal and lingual surfaces. Then, teeth were divided into 3 groups. Adhesives used in this study were Excite (Ivoclar/Vivadent), AdheSE(Ivoclar/Vivadent) and AdheSE-one Ivoclar (Vivadent/Vivadent). After application of adhesives, cavities were restored with a resine composite (InTen-S A1/ Ivoclar), in 3 increments and cured with QTH light curing unit (700 mW/cm). After 24 hours storage of teeth in 370C water, teeth were thermocycled (500 cycles in 5-550C) and stored in 1% basic fushin for 24 hours. After that, the specimens were rinsed with running water and mounted in a self-cured acryl. Finally, the specimens were sectioned and maximum depth of dye penetration for each restoration was measured using stereomicroscopy. The results were statistically analyzed with Mann-Whitney U test.
Results: In comparison between enamel and dentin margins in each group, microleakage in enamel margins were less than that of dentin margins. This difference was statistically significant in Excite and AdheSE-one groups (P=0.001, P=0.043). AdheSE showed the least microleakage in dentin margins however, there was no significant difference between 3 bonding agents (P=0.14). In enamel margins, there were significant differences between 3 bonding agents (P=0.001). Excite showed the lowest microleakage and AdheSE-one had the highest microleakage.
Conclusion: The least enamel microleakage was associated with the total-etch and least dentin microleakage was observed in the two-step self-etch adhesive system.

---

Background and Aims: The purpose of this experimental study was to investigate the shear bond strength of three new adhesive systems to enamel and dentin of permanent human teeth using three new etch and rinse and self-etch adhesive systems.
Materials and Methods: Sixty intact caries-free third molars were selected and randomly divided into 6 groups. Flat buccal and lingual enamel and dentin surfaces were prepared and mounted in the acrylic resin perpendicular to the plan of the horizon. Adhesives used in this study were Tetric N-Bond, AdheSE and AdheSE-One F (Ivoclar/Vivadent, Schaan, Liechtenstein). The adhesives were applied on the surfaces and cured with quartz tungsten halogen curing unit (600 mW/cm² intensity) for 20 s. After attaching composite to the surfaces and thermocycling (500 cycles, 5-55ºC), shear bond strength was measured using a universal testing machine at a crosshead speed of 0.5 mm/min. The failure modes were examined under a stereomicroscope. The data were statistically analyzed using T-test, one-way ANOVA, Tukey and Fisher's exact tests.
Results: In enamel, Tetric N-Bond (28.57±4.58 MPa) and AdheSE (21.97±7.6 MPa) had significantly higher bond strength than AdheSE-One F (7.16±2.09 MPa) (P<0.0001). Tetric N-Bond had higher bond strength than AdheSE but there was not any significant difference between them (P=0.093). In dentin, there were significantly differences among all adhesives (P<0.001). Tetric N-Bond (20.62±3.03 MPa) showed the highest and AdheSE-One F (6.54±1.13 MPa) had the lowest value. The bond strength in enamel was higher than that observed in dentin and the difference was significant in Tetric N-Bond (P=0.044) and AdheSE (P=0.000) groups. There were no significant differences in the mode of failures among groups (P>0.05).
Conclusion: Shear bond strength to dentin in Tetric N-Bond (etch and rinse system( was higher than self-etch adhesives (AdheSE and AdheSE-One F). The bond strength to enamel and dentin in two-step self-etch (AdheSE) was higher than one-step self-etch (AdheSE-One F).