Journal of Dental Medicine

  Background and Aims: The purpose of this study was research on a new herbal compound (Seidlitzia Rosmarinus) made by Traditional Medicine Research Group, University of shahed to find a safer alternative to HCL-Pumice compound technique.

  Materials and Methods: In this randomized clinical trial seventy two anterior teeth from 9 patients were divided in to three groups according to fluorosis severity: mild (34 teeth), moderate (14 teeth), and sever (24 teeth). In each patient, half of the teeth were treated with “Shahed” compound and other half treated with HCL-Pumice compound. Before and after treatment, photographs were taken in both groups. HCL-Pumice treatment compound was applied for 30 seconds periods and continued for 10 minutes if necessary. In case of herbal Shahed compound the time was determined by clinical symptoms or when labial contour was dismissed, If the result was not esthetistically acceptabale for the patient, HCL-Pumice compound was applied on teeth. NaF was applied after mouth washing. The photographs of the teeth before and after treatment were reviewed by two experienced observer unaware of the treatment modality. The results were analyzed using willcoxon^’s, kruskal-wallis and scheffe test.

  Results: There was over 81.3% acceptance between two observers and no significant differences in intraobservers evaluation (P>0.05). Improvement in beauty indexes were observed in all degrees of dental fluorosis by 18% with HCL-Pumice compound application, but “Shahed” herbal compound induced significant reduction in the amount of white spots in mild fluorosis and stain intensity of moderate fluorosis (P<0.05) , while the reduction in the severity of discoloration in group 2, these two techniques were statistically equivalent but in the remainder, HCL-Pumice compound was more significantly effective (P<0.05) .

  Conclusion: HCL-Pumice compound reduces the severity of the discoloration of the teeth. Shahed herbal compound cannot reduces the discoloration like as HCL-Pumice compound.

  Background and Aims: Metallic nano-particles show exclusive biological, chemical and physical characteristic. The purpose of this research was to evaluate the effect of various amounts of nanosilver incorporation (0 (as control), 20, 40, 80, 120, 200 ppm) on the mechanical Properties ( compressive and flexural strength) of resin modified Glass ionomer Cement.

  Materials and Methods: Based on ISO 4049 and ISO 9971 for polyalkenoid cements, 90 cases in each group were prepared for the flexural and compressive strength. Specimens in 6 groups with different amounts of nanosilver (20, 40, 80, 120 and 200 ppm) and control (Fuji II LC improved), stored in distilled water at 37 ° C for 1 day and 30 days. Flexural strength, using a three-point bending method, Modulus of elasticity and the compressive strength were measured by universal testing machine (Zwick) with crosshead speed of 0.5 mm/min. Data were analyzed using two-way ANOVA and Tukey post HOC test.

  Results: The flexural strength and modulus of various amounts of nanosilver incorporation of resin modified glass-ionomer cement were not significantly different (P>0.05). The compressive strength of incorporating of
20 ppm compared with control (P=0.01), 40 ppm (P=0.02) and 80 ppm compared with control (P<0.001) were increased. The flexural strength and compressive strength of Fuji II LC, containing nanosilver particles were increased after 1 day and 1 month significantly (P<0.001).

  Conclusion: Incorporation of 20 to 80 ppm nanosilver into Fuji II LC had increased mechanical properties compared to the original cement.

  Background and Aims: Dental caries is one of the most common infectious diseases which could be prevented in various ways. The aim of the present study was to evaluate the effect of a toothpaste containing different concentrations of nano-hydroxyapatite on the remineralization of incipient caries.

  Materials and Methods: 9 sound first premolar teeth of maxilla and mandible were sectioned to four pieces. 6 specimens were stored in distilled water as control group. The remaining 30 specimens were demineralized for 72 hours and then their microhardness was measured. 0, 0.5, 1, 2 and 5% wt nano-hydroxyapatite were added to the solution of distilled water and toothpaste. Specimens were divided into 5 groups (N=6) and after demineralization, each group were randomly immersed in the above-mentioned solutions for 15 minutes. Next, specimens were kept in artificial saliva for 1 hour followed by immersion in the related remineralizing solution for another 15 minutes. This procedure was repeated for 5 days. Finally, the microhardness of the teeth was measured. Data were analyzed using repeated measures analysis of variance (ANOVA).

  Results: The microhardness of demineralized teeth was increased following exposure to different concentrations of nano-hydroxyapatite, but this increase was not statistically significant (P=0.62).

  Conclusion: Nano-hydroxy apatite can enhance remineralization and increase the tooth microhardness although this increase was not significant.