Journal of Dental Medicine

Dentin bonding agents create stronger bonding between dental composites and dentin. But, none of them can prevent the microleakage. The important factors of progressing microleakage are the stress of polymerization shrinkage of resin composite and removal of smear layer in total-etch technique. The aim of this study was the evaluation of the effect of experimental method (modifying smear layer and etching of enamel margin) and comparison with the total-etch technique. In this experimental method, 60 extracted human molar teeth were disinfected. Then, class 5 cavities were prepared on the buccal surface and 1 mm above CEJ. The specimens were divided randomly to 6 groups with iO samples in each group. The specimens groups were:
1- Scotchbond Muiti- Purpose Plus Adhesive System (S.B.M.P.P) +Tetric composite
2- S.B.M.P.P + Ariston composite
3- Ariston liner + Ariston composite
4- S.B.M.P.P without enamel and dentin etching + Tetric composite + rebonding with Flowable Tetric
5- S.B.M.P.P without enamel and dentin etching + Ariston composite + rebonding with Flowable Tetric
6- S.B.M.P.P without enamel and dentin etching + Tetric composite
After finishing and polishing, the specimens were termocycled, stained with fushin, sectioned within the specimens and evaluated for dye penetration with stereomicroscope. Wilcoxon Sign and Kruskal Wallis tests were used for statistical analysis.
Results showed that group 3 had microleakage more than groups of 1, 2 and 5 (P<0.0 5) and this difference was significant. There was no significant difference among the other groups.

Background and Aims: Moisture contamination of etched enamel during application of sealant is the most frequently cited reason for sealant failure. In previous studies, some hydrophilic bonding agents have been shown to bond to etched enamel after salivary contamination. The purpose of this study was to evaluate the enamelsealant interface following the use of primer on the saliva contaminated and/or moist etched enamel.

Materials and Methods: 40 extracted human incisors were selected. The enamel surfaces were etched for 20 seconds with an acid gel and rinsed for 30 seconds and dried until chalky surface was observed. Teeth were randomly divided into four treatment groups (n=10). Sealant (Deguseal mineral, Degussa) was applied on (1) etched enamel surface as a standard control group, (2) in conjunction with using primer material on moist etched enamel, (3) in conjunction with using primer material on salivary contaminated etched enamel, and (4) on wet contaminated etched enamel surface as a negative control group. Then, the specimens were observed with scanning electron microscopy (SEM) at ×1400 magnification. To evaluate the enamel resin interface, the number of resin tags was counted. Data were analyzed using one-way ANOVA.

Results: The results showed that primer used on moist enamel under sealant had no significantly difference in number and shape of tags in comparison with standard group (P>0.05). Application of primer on saliva contaminated enamel surface under sealant significantly reduced the number of tags and changed the shape and pattern of tags (P<0.001). Following application of sealant on contaminated and etched enamel alone, no resin tags formed.

Conclusion: Application of primer relatively reduced sensitivity to saliva contamination but the pattern was changed and number of tags reduced. Therefore, primer application might be useful whenever the isolation is not possible. However, it should be emphasized that restrict isolation in sealant therapy is recommended.

Background and Aims: The purpose of this in vitro study was to assess the effect of two different surface treatments on the contrast ratio of IPS e.max press ceramic submitted to accelerated aging.

Materials and Methods: Ten ceramic (IPS e.max Press) disks (10-mm diameter and 1.5-mm thick) were fabricated according to the manufacturer's recommendations. The samples were randomly divided into 2 groups (n=5): polishing and glazing. Contrast ratio ware obtained with a spectrophotometer before and after accelerated aging. The contrast ratio (CR=Yb/Yw), was defined as the ratio of illuminance (Y) of the test material when it is placed on the black background (Yb) to the illuminance of the same material when it is placed over a white background (Yw), was determined. The data were statistically analyzed by two-way analysis of variance (P<0.05).

Results: All specimens of IPS e.max press ceramic showed significant increase in CR after 300-hour accelerated aging time (P=0.005). Polished samples showed significantly higher opacity compared with that of the glazed ones (P=0.018).

Conclusion: Within the limitations of this study, it may be concluded that the glazed specimens showed higher stability in their translucency than the polished specimens.