Showing 6 results for Adhesives
M. Mortazavi , Z. Bahrololoomi ,
Volume 16, Issue 1 (4-2003)
Abstract
Statement of Problem: Microleakage presents the major cause for restorations failure in the oral cavity resulting in postoperative sensitivity, pulp irritation and secondary caries formation.
Aim: The aim of this study was to compare two dentinal adhesive systems of fifth generation and copalite varnish in reducing microleakage of amalgam restorations in primary teeth.
Materials and Methods: In this in-vitro study, 100 class V amalgam restorations were prepared on the buccal or lingual surfaces of primary molar and canine teeth. Samples were randomly divided into four groups (25 samples each). No liner was used for the first group and the second group restorations were lined with copalite varnish. Two dentin adhesives, called Syntac C and Single Bond, were used for the third and fourth groups, respectively. At the next stage, the samples were immersed in 5% fuschin solution for 24 hours, then sectioned buccolingually, and examined under a stereomicroscope for microleakage evaluation.
Results: There was a significant difference between four groups statistically (PO.000I), Comparing four groups, the first and fourth ones, demonstrated the most and the least microleakage, respectively.
Conclusion: The present study showed that new dentinal adhesive systems caused microleakage reduction in amalgam restorations of primary teeth.
M. Ghavam-Nasiri , F. Malek-Nejad , A. Rohani , M. Akbari ,
Volume 16, Issue 2 (5-2003)
Abstract
Statement of Problem: A lot of efforts have been made to create a complete adaptation between tooth and amalgam restorations.
Purpose: The aim of this study was to evaluate microleakage and interfacial micromorphology of amalgam restorations lined with dentin adhesives, namely One Coat Bond, Syntac, Excite and Copalite,as liners.
Materials and Methods: 144 intact human canine teeth were selected. Then class V cavities, with enamel and dentinal margins, were prepared on each of them. Cavities were lined with different dentin bonding systems (Syntac, One Coat Bond and Excite) according to the manufacturer's instructions and restored with Oralloy and Cinalloy, non gamma 2 spherical amalgams and Aristaloy a non gamma 2 Admixed alloy. Copalite was used in the group, served as controls. After thirty days storage in synthetic saliva at 37°c, the specimens were thermocycled in saliva (4000 cycles). The degree of microleakage was assessed by means of basic fushin dye penetration and recorded. The gap width was evaluated with Scanning Electron Microscope. Pearson and %2 tests were used to analyze the results.
Results: None of the systems, tested in this study, eliminated microleakage completely, Pearson's correlation coefficient showed a positive correlation between gap and microleakage (P<0/05).Statistical significant differences were revealed among the liners regarding gap and microleakage (P<0.05).One Coat Bond and Syntac appeared to leak less than other groups. The gap width by One Coat Bond and Syntac were respectively 0.35 and 0.3 urn in dentine, 0.2 and 0.1 in enamel. Excite and copalite gap width in dentine and enamel were 1,3-1.36 urn and 0.3-0.6, respectively. The type of amalgam did not have any effect in the degree of microleakage and gap width (P>0/05).
Conclusion: One Coat Bond and Syntac, comparing to Excite and Copalite, showed less microleakage and gap width.
M. Ghavam, S. Arami, M. Reshad, M. Imani, M. Ataei, M. Mirzaei, E. Yasini, M. Hasani Tabatabaei, A. Pahlavan, H. Kermanshah ,
Volume 22, Issue 4 (1-2010)
Abstract
Background and Aims: In spite of the advances achieved in the field of dentin adhesives, the longevity of bond to dentin is still a challenge. According to recent studies, Matrix Metaloproteinase (MMP) inhibitors can increase clinical longevity of bonding and decrease leakage. The aim of this study was to evaluate the amount and pattern of doxycycline release from an experimental dentin adhesive containing this MMP inhibitor.
Materials and Methods: In this experimental study, specimens containing 0.25 and 0.5 loading percent of doxycycline in an experimental monomer were prepared in cylindrical moulds of 12 mm diameter and 2 mm thickness. The adhesive monomer was composed of 12 wt% Bis-GMA, 10 wt% TMPTMA, 28 wt% HEMA and 50 wt% ethanol. Camphorquinone and amine were used as initiators.
Results: Addition of 0.25 and 0.5 w% doxycycline showed linear release in both groups. Increasing the loading percent of doxycycline caused more release. The release continued during the test period.
Conclusion: Doxycycline release was observed from the experimental adhesive. Further studies in this field will help in preparing adhesive systems with more clinical longevity.
Davari Abdolrahim , Kazemi Alireza Danesh , Mousavinasab Majid , Mohammadi Najmeh Pour ,
Volume 26, Issue 3 (8-2013)
Abstract
Background and Aims: Different adhesives with different solvents may have different solvent evaporation rates. The purpose of this study was to evaluate the solvent evaporation in the self etch and total etch adhesive in different air drying times.
Materials and Methods: Five adhesives were used in this study: Excite, Prime & Bond NT, UNO, Single Bond, SE Bond Primer. Twelve drops of each adhesive were used for each period of air drying (5, 15, 30 sec). The percentage of mass loss was measured during each test. Data were analized using two-way ANOVA and Tukey.
Results: Acetone base adhesives showed more loss of mass than other adhesives (P<0.01). P&B NT showed more loss of mass than other adhesives in all air drying times (P<0.01). Adhesives showed different evaporation rates in different air times (P<0.01).
Conclusion: Adhesives with acetone/water or alcohol/water solvent shows more stable behavior in comparison with adhesives containing pure aqueous solvents.
Mehran Bahrami, Maryam Memarian, Farinaz Khodadad Kashi,
Volume 28, Issue 3 (10-2015)
Abstract
Background and Aims: Residual ridge resorption is an unpredictable, unavoidable and time-dependent process which occurs in denture-wearing patients especially those who use mandibular dentures. This process causes more problems in mandible because of its less support, tongue forces and more resorption. Inserting implants in many of these patients requires bone grafts. Overdentures are also more expensive. Denture adhesives are the last option to improve retention and masticatory function in denture-wearers with severe resorption of alveolar ridge. Nowadays only a few denture adhesives are used in Iran and there is not much information about their standard features including, pH, bond strength and washability. The objective of this study was to examine and compare the mentioned characteristics of four denture adhesives (Professional, Corega, Fittydent and Fixodent) and to introduce the most suitable denture adhesive for clinical use.
Materials and Methods: All the methodologies of ISO 10873:2010 were applied. To measure the pH value, 1±0.1g of each denture adhesive was diluted with 5g of propylene glycol and mixed with water. Using pH meter, pH of each group was measured separately for 4 times (n=4) and results were recorded. For the washability test, 4 dentures were fabricated (n=4) and each group of denture adhesives was placed on a denture according to manufacture instructions. For simulating mouth environment specimens were placed in water at 37±2 ̊C bath for 1 hour and then washed with a plastic brush. Specimens were examined for any residual adhesive and the results were recorded. For bond strength test, a sample holder was gently filled with denture adhesives and was attached to the holding arm of bond strength testing device (Santam, STM 20, Iran). Specimens were placed in 300ml water bath at 37±2 ̊C for 10 minutes, and then shaken to be dried and placed in the bond strength testing device. 10N force with 5mm/min rate was applied to the specimen. The force was maintained for 30s and then device arm was pulled back and the highest number was recorded with computer software (Santam Machine Controller v4.19, Iran). The test performed 8 times (n=8) for each adhesive and 8 results were recorded. Data were analyzed using ANOVA test for comparing the bond strength with a significant level fixed
at 0.05.
Results: Professional and Corega adhesives had more neutral pH than that of Fittydent and Fixodent which were more acidic. Washability test showed no remaining mass of any adhesive and there was not any statistically significant difference between groups (P>0.05). Fittydent and Corega adhesives showed higher bond strength than that of Professional and Fixodent and this difference was statistically significant (P<0.05).
Conclusion: Professional and Corega adhesives had less acidity. Thus they cause less harmful effects on the oral mucosa than that of Fittydent and Fixodent and should be indicated in patients with little-tolerant oral mucousa such as diabetous, iron-deficiency anemia and hypertention. All the groups had acceptable washability. Fittydent and Corega had higher bond strength than that of Professional and Fixodent. Therefore in complete-denture-wearers who require more retention as a result of severe ridge resorption, macrotruma, and maladaptiivity, Fittydent and Corega seems to be more acceptable.
Elahe Soltanmohamadi Borujeni, Ali Bavi, Mohammad Aghaali, Ali Saleh, Aida Mehdipour,
Volume 37, Issue 0 (3-2024)
Abstract
Background and Aims: Strong bond between the ceramic brackets and ceramic veneers has an important role in cosmetic treatment. The purpose of this study was to investigate the effect of aging on the shear bond strength (SBS) of ceramic brackets bonded to zirconia after surface preparation by Neodymium-doped Yttrium Aluminum Garnet (Nd: YAG) laser or sandblasting with alumina.
Materials and Methods: This experimental study was conducted on 24 zirconia blocks and these blocks were randomly divided into two groups for surface preparation and each was sub-divided into three time intervals. Surface preparation was done by sandblasting with alumina: in SG1 (Immediately after sandblasting), SG2 (2 weeks after sandblasting), and SG3 (3 months after sandblasting) groups. For the Nd: YAG laser (1/5W, 20Hz, 10s) with non-contact mode: in LG4 (Immediately after laser), LG5 (2 weeks after laser), and LG6 (3 months after laser) groups. The ceramic brackets were bonded to the zirconia blocks. The SBS and adhesive remnant index (ARI) were evaluated and compared among test groups. Dara were analyzed using Mann Whitney test.
Results: There was no significant difference between the SBS of SG1 and LG4 (P=0.430), SG2 and LG5 (P=0.382) and SG3 and LG6 (P=0.326) groups. LG4 group showed the highest shear bond strength. After aging (2 weeks and 3 months), the laser groups showed higher SBS. There was no significant difference in the ARI between SG1 and LG4 (P=0.220), SG2 and LG5 (P=0.154), SG3 and LG6 (P=0.527) groups.
Conclusion: No significant difference was observed between the Nd: YAG laser and sandblasted groups in terms of SBS and ARI over time. Therefore, Nd: YAG laser could be used as a surface treamnet method in Zirconia crowns for bonding to ceramic brackets.