Journal of Dental Medicine

 Polymerization shrinkage of light cure composite resins causes many complications in conservative and esthetic restorations. The objective of this in-vitro study was to evaluate the polymerization shrinkage, degree of conversion and the amount of filler in IDM and tetric ceram composites. Ten disk shaped, uncured specimens (8mm×1.547mm) of each composite were placed on glass slide in the center of the metal attached to it. Then specimens were light cured for 60s from underneath. After 30 minutes, the thickness of specimens, using a micrometer and the percent of the polymerization shrinkage of each sample were measured. Statistical analysis was carried out by t-test (P<0.05). Also the degree of conversion of specimens was evaluated with FTIR and the mineral filler content was measured by burning in electric oven. Polymerization shrinkage in IDM and tetric ceram was not significantly different. Degree of conversion and mineral filler content in tetric ceram was greater than that of IDM.

It is assumed that the low degree of conversion in IDM is due to its chemical composition and filler content. Also, the similarity in linear polymerization shrinkage between IDM and tetric ceram may be caused by the low degree of conversion in IDM.

Statement of Problem: Recently, investigators have presented new methods to reduce polymerization shrinkage of composite resin restorations. It is claimed that more powerful light cure systems associated with a change in radiation patterns, lead to improved mechanical properties and reduced microleakage.

Purpose: The aim of the present study was to evaluate the effects of two curing systems, known as Soft-Start, Pulse-Delay, on microleakage and degree of conversion of composite resin restorations.

Materials and Methods: To evaluate microleakage, dye penetration method in class V cavities was applied. 30 extracted human molars filled with three different curing techniques, namely conventional, Soft-Start and Pulse-Delay, were compared. Degree of conversion was measured by FTIR Spectroscopy method immediately after sample curing. Kruskal- Wallis and Mann-Whitney test were used to compare groups.
Results: The degree of microleakage in enamel and dentin among three groups was not significantly different, however, microleakage in gingival and occlusal walls showed a significant difference among Pulse-Delay curing (P=0.001) and Soft-Start curing (P=0.28) groups, meaning that leakage gingival in wall was significantly higher than occlusal wall. This difference was not significant in conventional group. Moreover, the degree of conversion was not statistically significant among three groups (P-0.909).
Conclusion: Soft-Start and Pulse-Delay curing systems, with a two intensity start curing light, do not provide better marginal adaptation in class V composite resin restorations. It should be mentioned that polymerization degree is not also reduced in these methods.

Statement of Problem: The quantity of remaining unreacted double bonds may be a significant factor pertaining to the mechanical, physical and chemical properties of restorative resins. Insufficient polymerisation within the hybrid layer may cause significant differences in the quality of this layer, and act as a reservoir for monomer release thus increasing cytotoxic potential.

Purpose: The aim of this study was to measure the degree of conversion of three generations of 3M dentin bonding agents and an experimental dentin bonding agent

Materials and Methods: The quantity was determined from the transmission IR-spectrum of the materials before and after polymerization. ScotchBond MP plus adhesive, SingleBond, Prompt L-Pop, and an experimental dentin bonding were used to measure degree of conversion. Six repetitions of each bonding were investigated. Time of light curing was 120s. Kruskal-Wallis and Mann-whitney test were used to compare groups with P<0.05 as the limit of significance.

Results: The results showed a significant difference between groups (P<0.01). A trend of increasing in Singlebond conversion obtained in comparison with ScotchBond MP plus adhesive, Prompt L-Pop and experimental dentin bonding. The degree of conversion was not statistically significant among the other dentin bondings. No significant difference was found between conversion of the experimental dentin bonding and ScotchBond MP plus adhesive (P=1.00) with P<0.05 as the limit of significance.

Conclusion: Dentin bonding technology continues to evolve toward simpler systems. However, Prompt L-Pop as a self-etching adhesive does not show the trend of increasing the degree of conversion. However, the performance of these simpler systems must be further investigated.

Background and Aim: Insufficient polymerization of resin cements is of considerable clinical importance, because of mechanical deficiencies and biological side effects of uncured resin. Dual cure resin cements are getting popular in luting tooth colored posts and although their curing is claimed to proceed chemically, polymerization efficiency in deep areas of canal is uncertain. The aim of this study was to evaluate degree of polymerization of dual-cure resin cements used for luting translucent and opaque fiber posts in different distances from the light tip.

Materials and Methods: In this experimental in vitro study, degree of conversion of two dual cured resin cements, Rely X ARC (3M, ESPE) and Nexus 2 (Kerr, USA) were measured when used with DT-Light and DT-White posts (RTD, France). The light curing unit used was Optilux 501, with output of 650-700 mw/cm2 with emitting time of 60 seconds. Degree of conversion was measured in three different depths (4, 6, 8 mm) by FTIR. The data were analyzed using ANOVA and Post hoc tests. P<0.05 was considered as the level of significance.

Results: DC% of Rely X with either of the posts was not significantly different in the studied depths (P>0.05). Nexus used with DT-Light had lower DC% in 8 mm depth (P<0.05). Nexus used with DT-White showed lower DC% in 8 mm depth compared to 4 mm depth. The control groups of both cements showed significant increased DC% in 4 mm depth compared to 6 and 8 mm depths (P<0.05). DT-White caused decreased DC% in both cements in 4 mm. DT-Light caused increased DC% of Rely X in 6 mm depth compared to DT-White and control. DT-Light increased DC% of Nexus in 6 and 8 mm depths, compared to DT-White and control groups.

Conclusion: Based on the results of this study, application of translucent fiber posts has a significant effect on degree of polymerization in dual-cure resin cements, compared to opaque types. Their better light transmission to deep areas due to the effect of optical fibers, can lead to better results.

Background and Aim: Halogen lamp is the commonly used light source for composite photo polymerization. Recently, high power halogen lamps, LED and plasma arc are introduced for improving the polymerization. The aim of this study was to investigate the effect of conventional and high power halogen lamps and LED light curing unit on degree of conversion of two different composite resins.

Materials and Methods: In this in vitro experimental study two halogen units (Coltolux 50 with the intensity of  330 mW/cm² and Optilux 501 with two different operating modes of standard with the intensity of 820 mW/cm² and Ramp with the intentsiy of 100-1030mW/cm²) and one LED light curing unit (620 mW/cm²) were used. The composites were hybrid (Tetric ceram) and nanofilled (Filteke supreme). Each materials/curing method contained three samples and degree of conversion (DC) was measured with FTIR. Data were analyzed statistically with one way and two way ANOVA, Tukey HSD. P<0.05 was considered as the limit of significance.

Results: Tetric ceram revealed higher DCthan Supreme. Tetric ceram showed a significant decrease in DC when Coltolux 50 was used in comparison to LED and Optilux 501. The latters did not show significant effect on DC of this material. DC of Supreme polymerized with various curing modes was not significantly different.

Conclusion: Based on the results of this study, degree of conversion in hybrid composites was higher than nanofilled. In comparison with conventional halogen lamp (Coltolux 50), high intensity halogen lamps and LED unit significantly lead to higher degree of conversion in hybrid composites.

Background and Aim: Nonmetallic tooth- colored posts adhere to canal walls by dentin bonding agents and resin cements. Better retention and proper distribution of stress result from enough and proper bonding. The purpose of this study was to evaluate bond strength of D.T. Light - post with two different resin cements (self-cure & dual-cure) and to investigate the effect of irrigating solutions applied in root canal on bond strength of the resin cements and D.T.Light- post to root canal wall.

Materials and Methods: In this experimental study 40 single root teeth (maxillary canine & central) were selected and stored in 0.1% thymol solution for one week and transferred to distilled water. The teeth were decoronated 2mm above CEJ. The canal space was mechanically enlarged using k-files (up to # 70). The teeth were randomly divided into two groups. The first group was irrigated with 2.6% NaOCl, and the second was irrigated with normal saline. After drying, the teeth were filled with gutta percha cones using lateral condensing method. After two weeks the post space was prepared and D.T.Light- post was inserted in each subgroup using self or dual-cure cements according to manufacturer's instructions. After thermocycling, the apical part was cut 1cm below CEJ. The remained length was divided into 9 equal sequential sections. Each section was submitted to shear push-out test in universal testing machine. Statistical analysis of the bond strength data was performed using ANOVA and post hoc tests with p<0.05 as the level of significance. All failed specimens were examined under stereomicroscope. Degrees of conversion of the cements were determined by FTIR.

Results: Significant difference in bond strength values were found among sites (P=0.001) and cements (P=0.03). With increasing in depth, bond strength decreased. The mean bond strength value in dual-cure resin cement was higher than self-cure cement. The irrigating solutions caused no significant difference in bond strength (P=0.46). DC% had significant difference in various depths.

Conclusion: According to the results of this investigation, bond strength of dual-cure cement is higher than self-cure one in D.T Light- post because of post's translucency. 2.6% sodium hypochlorite does not affect the bond strength.

Background and Aim: In spite of the achievements in the field of dental adhesives, we are facing challenges with dentine bonding resistance, strength and stability. According to recent studies the role of MMP inhibitors in association with bonding^,s persistence and leakage reduction and restoration^,s persistence is important. The aim of this study was to investigate the effect of doxycycline as a MMP inhibitor on the degree of conversion (DC) of an experimental dental adhesive.

Materials and Methods: In this experimental study, a new dental adhesive blend was prepared by mixing doxycycline monohydrate (in concentrations of 0.0, 0.25, 0.5, and 1 wt.%) with monomers. The monomers were composed of 12% Bis-GMA and 10% TMPTMA, 28% HEMA, and 50% Ethanol by weight for all groups. Comphorquinone and amines were chosen as photo initiator system. Degree of conversion of all adhesives was measured using FTIR spectroscopy. The results were analyzed using one-way ANOVA and Tukey post hoc tests.

Results: The results showed that addition of 0.25, 0.5, and 1 weight percent doxycycline did not significantly reduce the DC of the adhesives compared to 0.0% control group (p>0.05%).

Conclusion: According to the results of this study, adding doxycycline to the adhesives did not adversely affect the DC.