Dentin bonding agents create stronger bonding between dental composites and dentin. But, none of them can prevent the microleakage. The important factors of progressing microleakage are the stress of polymerization shrinkage of resin composite and removal of smear layer in total-etch technique. The aim of this study was the evaluation of the effect of experimental method (modifying smear layer and etching of enamel margin) and comparison with the total-etch technique. In this experimental method, 60 extracted human molar teeth were disinfected. Then, class 5 cavities were prepared on the buccal surface and 1 mm above CEJ. The specimens were divided randomly to 6 groups with iO samples in each group. The specimens groups were:
1- Scotchbond Muiti- Purpose Plus Adhesive System (S.B.M.P.P) +Tetric composite
2- S.B.M.P.P + Ariston composite
3- Ariston liner + Ariston composite
4- S.B.M.P.P without enamel and dentin etching + Tetric composite + rebonding with Flowable Tetric
5- S.B.M.P.P without enamel and dentin etching + Ariston composite + rebonding with Flowable Tetric
6- S.B.M.P.P without enamel and dentin etching + Tetric composite
After finishing and polishing, the specimens were termocycled, stained with fushin, sectioned within the specimens and evaluated for dye penetration with stereomicroscope. Wilcoxon Sign and Kruskal Wallis tests were used for statistical analysis.
Results showed that group 3 had microleakage more than groups of 1, 2 and 5 (P<0.0 5) and this difference was significant. There was no significant difference among the other groups.

Background and Aim: Fractured anterior teeth can be restored by adhesive bonding of the separated fragment to the remaining tooth structure. This invitro study evaluated the force required for fracture of rebonded fragments which were dried and rewetted for various time intervals prior to bonding.

Materials and Methods: One hundred and eight human mandibular incisors were selected and were divided into 9 groups and then were fractured. The fragments were stored in air at room temperature and ambient humidity. They were air dried for 30 minutes in group 1, 2 and 3,  6 h in group 4 and 5,  24 h in group 6 and 7, and 3 days in groups 8 and 9. The apical parts of the fractured teeth were stored in water.After storage in air, each fragment in group 1 was bonded to the remaining apical tooth structure with a bonding agent and flowable composite.In groups 2, 4, 6 and 8 after air drying the fragments were stored in water for 30min. The time of storage in water in groups 3, 5, 7, 9 was 24 hours. Then each fragment was bonded to the apical part structure. The mean force required for fracture was measured by a mechanical testing machine. One way ANOVA and Tuckey tests were used for analysis.

Results: There were statistically significant differences between different groups (p<0.001).The highest and lowest force required for fracture belonged to groups 3 and 8 respectively. The force required for fracture in group 1 was lower than group 2, 3, 5 and 7 and 9 and more than groups 4,6 and 8 with significant differences.While there were no significant differences among groups 3, 5, 7, 9 and 4, 6, 8 the force required for fracture in groups 2, 3, 5, 7 and 9 was more than 4, 6, 8 with significant differences.

Conclusion: This research revealed that the force required for fracture was affected by air storage of fragments prior to bonding. Also showed that with an increase in duration of drying the force required for fracture decreased and after a period of time it becomes steady. This study showed that in order to increase the fracture strength after air drying the fragment should be immersed in water for at least 24 hours prior to bonding.

Background and Aim: Evaluation of shear bond strength and microleakage of bonding agents is important as these properties play main roles in adhesion of composite to dental tissues. Microleakage results in bacterial penetration into dentin tubules and enamel surfaces and causes sensitivity and recurrent caries followed by destruction of composite filling. Insufficient shear bond strength results in early failure of filling in low masticatory forces. The main goal of this study was to compare the microleakage and shear bond strength of an experimental adhesive and Scotchbond multi-purpose (MP) adhesive system.
Materials and Methods: In this experimental study, sixty extracted caries free human molar teeth were randomly assigned into 4 groups of 15 each for shear bond strength. Variables were bonding agents, enamel and dentin. Twenty teeth assigned into 2 groups of 10 each were used for valuation of the microleakage. Microleakage and shear bond strength were performed according to ISO TR 11405. All data were analyzed with parametric and non-parametric tests according to their normality distribution. Also, Weibull distribution performed on data.
Results: Data obtained from both microleakage and shear bond strength tests showed no significant difference between the experimental bonding and Scotchbond MP bonding (P>0.05). Furthermore, there was no significant difference between the microleakage of occlusal and gingival parts of both bondings (P>0.05).
Conclusion: Experimental adhesive bonding showed acceptable results regarding microleakage and shear bond strength. It may be concluded that the experimental dentin bonding had a comparable performance quality with that of commercial system.

Background and Aims: The aim of this in vitro study was to assess the shear bond strength of amalgam to dentin using four dentin adhesive systems.
Materials and Methods: One hundred human molars were selected. After enamel removal, a dentin cylinder with 3 mm thickness was prepared. Eighty specimens were resorted with amalgam and four dentin adhesive systems as follows (n=20): group 1, Scotch Bond Multi-Purpose group 2, One Coat Bond group 3, PQ1 and group 4, Panavia-F. In group 5, 20 specimens were resorted with amalgam and varnish as control group. The specimens were incubated at 37°C for 24 h. The shear bond strengths were then measured by using push out method. The data were analyzed by one-way ANOVA and post hoc Duncan's tests.
Results: Mean values for bond strengths of test groups were as follows: group 1=21.03±8.9, group 2=23.47±9, group 3=13.16±8.8, group 4=20.07±8.9 and group 5=14.15±8.7 MPa±SD. One-way ANOVA showed the statistically significant difference between the bond strengths of five groups (P=0.001). Post hoc Duncan's test showed significant difference between groups 1and 3 (P=0.008), groups 1 and 5 (P=0.019), groups 2 and 5 (P=0.0008), groups 4 and 5 (P=0.042), and groups 3 and 4 (P=0.018).
Conclusion: Results of this study showed that the bond strength of amalgam to dentin using One Coat Bond as dentin adhesive system was higher than that observed in other dentin adhesive systems.