Showing 5 results for Dentin Adhesive
F. Maleknejad , Aa. Hoseini , M. ghawamnasiri , T. salari ,
Volume 15, Issue 2 (5-2002)
Abstract
Composite resin restorative materials, that nowadays are used as tooth-colour materials, have both benefits and weaknesses. One of these weaknesses is the contraction resulted from resin polymerization which influences on the composite dentin bond strength and it has been tried to be eliminated by different bonding systems. The aim of this in-vitro study was to compare the dentin bond strength of two dentine adhesive systems: multi-step Scoth Bond Multipurpose (SBMP) and single- step Excite, by two composites of Ideal Makoo and Tetric. One hundred sixty (160) sound human molars were selected. At first they were debrided and mounted with acrylic resin in molds. The enamel of the buccal surface was eliminated by diamond burs. To provide a flat dentin surface, it was removed about lmm. Then, based on the type of dentin adhesive, they were divided into two groups of 30 teeth and were applied on the exposed dentine surface according to the manufacturer's instructions. Then, each group was divided into two subgroups of 15, based on the type of composite resin. Cylinders of the desired composite resin, attached to the dentin surface, were used for 80 seconds. The samples were stored in 100% humidity (37°c) for 24 hours. The bond strengths was measured by a cross head blade with the speed of 2mm/min. Variance analysis and Duncan test, with 95% confidence level, showed that statistically, two factors of adhesive and composite, interact on each other, in bond strength. There was no significant difference in bond strength, between two composites with similar adhesives, however, comparing two different adhesives with the same composite, showed that the bond strength of Tetric with Excite (28.39) was more than that of SBMP (17.98 Mpa). Finally, it was recognized that among four experimental groups, there was only a significant difference in bond strengths, between Tetric-Excite with Tetric- SBMP. This study shows that dentin bond strength is influenced by dentin bonding agents, composite type and dentin structure, and using a type of composite with a dentin bonding agent, manufactured by the same company, results in a higher bond strength.
M. Ghavam-Nasiri , F. Malek-Nejad , A. Rohani , M. Akbari ,
Volume 16, Issue 2 (5-2003)
Abstract
Statement of Problem: A lot of efforts have been made to create a complete adaptation between tooth and amalgam restorations.
Purpose: The aim of this study was to evaluate microleakage and interfacial micromorphology of amalgam restorations lined with dentin adhesives, namely One Coat Bond, Syntac, Excite and Copalite,as liners.
Materials and Methods: 144 intact human canine teeth were selected. Then class V cavities, with enamel and dentinal margins, were prepared on each of them. Cavities were lined with different dentin bonding systems (Syntac, One Coat Bond and Excite) according to the manufacturer's instructions and restored with Oralloy and Cinalloy, non gamma 2 spherical amalgams and Aristaloy a non gamma 2 Admixed alloy. Copalite was used in the group, served as controls. After thirty days storage in synthetic saliva at 37°c, the specimens were thermocycled in saliva (4000 cycles). The degree of microleakage was assessed by means of basic fushin dye penetration and recorded. The gap width was evaluated with Scanning Electron Microscope. Pearson and %2 tests were used to analyze the results.
Results: None of the systems, tested in this study, eliminated microleakage completely, Pearson's correlation coefficient showed a positive correlation between gap and microleakage (P<0/05).Statistical significant differences were revealed among the liners regarding gap and microleakage (P<0.05).One Coat Bond and Syntac appeared to leak less than other groups. The gap width by One Coat Bond and Syntac were respectively 0.35 and 0.3 urn in dentine, 0.2 and 0.1 in enamel. Excite and copalite gap width in dentine and enamel were 1,3-1.36 urn and 0.3-0.6, respectively. The type of amalgam did not have any effect in the degree of microleakage and gap width (P>0/05).
Conclusion: One Coat Bond and Syntac, comparing to Excite and Copalite, showed less microleakage and gap width.
A. Makarem , M. Ghavam Nassiri , M. Esmaili ,
Volume 19, Issue 4 (1-2007)
Abstract
Background and Aim: Nanoleakage can cause discoloration around restoration margins, secondary caries, postoperative sensitivity and finally loss of restoration, thus adequate hybrid layer is of primary importance in prevention of nanoleakage in adhesive restorations. Because of structural differences between primary and permanent dentin, evaluation of nanoleakge in primary teeth is very important. The aim of this study was to evaluate the nanoleakage in composite restorations following application of self -etch and total-etch adhesives in primary and permanent teeth.
Materials and Methods: In this experimental study, Cl V cavities were prepared in buccal surfaces of 20 extracted primary molars and 20 extracted premolars. Each group was divided into 2 subgroups: In group (A), Gluma One Bond and in group (B), iBond adhesive materials were applied. After silver nitrate staining, specimens were mesiodistally sectioned and polished and then SEM examination was carried out to measure the nanoleakage .Data were analyzed statistically using, ANOVA and Duncan tests with p<0.05 as the limit of significance.
Results: Factors tested had no significant effect on each other. Primary teeth showed more nanoleakage than permanent teeth (P<0.05). Mean nanoleakage was significantly higher in cervical than occlusal margins (P<0.05) and also in iBond than in Gluma One Bond in primary teeth (P<0.05). In permanent teeth, the lowest nanoleakage was observed in Gluma One Bond.
Conclusion: The result of this study indicates that the use of total etch dentin adhesives (Gluma One Bond) in bonded restorations results in less nanoleakage in primary and permanent teeth.
M. Ghavam, M. Atai, M. Imani, M. Reshad,
Volume 22, Issue 2 (11-2009)
Abstract
Background and Aim: In spite of the achievements in the field of dental adhesives, we are facing challenges with dentine bonding resistance, strength and stability. According to recent studies the role of MMP inhibitors in association with bonding,s persistence and leakage reduction and restoration,s persistence is important. The aim of this study was to investigate the effect of doxycycline as a MMP inhibitor on the degree of conversion (DC) of an experimental dental adhesive.
Materials and Methods: In this experimental study, a new dental adhesive blend was prepared by mixing doxycycline monohydrate (in concentrations of 0.0, 0.25, 0.5, and 1 wt.%) with monomers. The monomers were composed of 12% Bis-GMA and 10% TMPTMA, 28% HEMA, and 50% Ethanol by weight for all groups. Comphorquinone and amines were chosen as photo initiator system. Degree of conversion of all adhesives was measured using FTIR spectroscopy. The results were analyzed using one-way ANOVA and Tukey post hoc tests.
Results: The results showed that addition of 0.25, 0.5, and 1 weight percent doxycycline did not significantly reduce the DC of the adhesives compared to 0.0% control group (p>0.05%).
Conclusion: According to the results of this study, adding doxycycline to the adhesives did not adversely affect the DC.
M. Ghavam, S. Arami, M. Reshad, M. Imani, M. Ataei, M. Mirzaei, E. Yasini, M. Hasani Tabatabaei, A. Pahlavan, H. Kermanshah ,
Volume 22, Issue 4 (1-2010)
Abstract
Background and Aims: In spite of the advances achieved in the field of dentin adhesives, the longevity of bond to dentin is still a challenge. According to recent studies, Matrix Metaloproteinase (MMP) inhibitors can increase clinical longevity of bonding and decrease leakage. The aim of this study was to evaluate the amount and pattern of doxycycline release from an experimental dentin adhesive containing this MMP inhibitor.
Materials and Methods: In this experimental study, specimens containing 0.25 and 0.5 loading percent of doxycycline in an experimental monomer were prepared in cylindrical moulds of 12 mm diameter and 2 mm thickness. The adhesive monomer was composed of 12 wt% Bis-GMA, 10 wt% TMPTMA, 28 wt% HEMA and 50 wt% ethanol. Camphorquinone and amine were used as initiators.
Results: Addition of 0.25 and 0.5 w% doxycycline showed linear release in both groups. Increasing the loading percent of doxycycline caused more release. The release continued during the test period.
Conclusion: Doxycycline release was observed from the experimental adhesive. Further studies in this field will help in preparing adhesive systems with more clinical longevity.